Titanium Dioxide A200 CAS 13463-67-7 for Enamel and Ceramic Glaze
Titanium Dioxide A200 is professional anatase titanium dioxide developed for enamel and ceramic glaze industry. Produced by sulfate process with controlled impurity content, it possesses excellent high‑temperature resistance and powerful opacifying performance. After high‑temperature firing, it delivers bright white glaze surface, improves covering capacity of enamel and ceramic glaze, reduces glaze transparency. It has good compatibility with feldspar, quartz and other glaze raw materials, stab
Product Overview
Titanium Dioxide A200 CAS 13463‑67‑7 is sulfate‑process anatase titanium dioxide dedicated to enamel and ceramic glaze. Optimized particle size distribution enhances opacifying effect after firing. This grade solves common industry pain points including insufficient glaze opacity, poor whiteness after firing and unstable glaze surface quality. It adapts to enamel frit smelting and ceramic glaze ball‑milling preparation production workflow.
Key Features
- Strong opacifying power, significantly improve covering performance of enamel and ceramic glaze.
- High whiteness after firing, obtain bright clean white surface for glaze and enamel layer.
- Excellent thermal stability, keep stable performance under high‑temperature frit melting and firing condition.
- Reasonable particle characteristic, good ball‑mill mixing performance with other glaze raw materials.
- Strictly controlled harmful impurities, reduce glaze surface defect risk such as black spots.
- Good compatibility with feldspar, quartz, borax and common ceramic & enamel raw materials.
Main Applications
‑ Opacifier for various enamel products: daily‑use enamel, industrial enamel frit‑ Whitening and opacifying additive for ceramic glaze‑ Sanitary ware ceramic glaze raw material‑ Art ceramic and craft ceramic glaze formula‑ Other enamel and ceramic products requiring high‑temperature opacifying agent
Usage Recommendation
‑ Recommended dosage: 3‑12 wt% in glaze or enamel frit formula, adjust according to target opacifying requirement.‑ Fully mix with other raw materials by ball milling for glaze slip preparation.‑ Follow corresponding firing curve according to enamel or ceramic technical specification.‑ Avoid mixing with other impurity‑containing raw materials during batching process.‑ Conduct small‑batch glaze formula trial firing before mass production.
Storage & Packaging
‑ Packaging: 25kg moisture‑proof kraft paper bag with PE inner liner.‑ Storage: Store in dry, cool and ventilated warehouse, keep tightly sealed against moisture absorption and foreign impurity contamination.‑ Shelf life: 24 months under standard storage conditions.
Previous : Anatase TiO2 KA100 CAS 13463-67-7 High Purity for Chemical Fiber
Next : Anatase TiO2 A300 CAS 13463-67-7 for Welding Electrode Coating
Copy product links
Long by picture save/share
Add Successfully
Add Successfully
Jishengya Technology
Shenzhen Jishengya Technology Co., Ltd. is located in Shenzhen, a special economic zone, and is a comprehensive technology enterprise integrating independent R&D, production and sales.
点击右上角
分享给朋友吧
Copyright © 2005-2026 Shenzhen Jishengya Technology Co., Ltd. All Rights Reserved.